“MCP HP510L” is a polypropylene homopolymer with good flow properties and is particularly suitable for the extrusion of film yarn, monofilament, cast film and sheet.
Characteristic Properties
MCP HP510L
- Outstanding processability, Good
- mechanical properties
Main Applications
Density: 0.9
- Fiber extrusion (Sheet, film yarn, monofilament), Cast film
- Baler twines, packaging twines and ropes
- Brush and broom filling and technical applications
- Coextruded film for packaging; Thin sheet for stationery folders
- Sheet for thermoforming; Gunny sacks
- Carpet backings, bags, industrial fabrics, mats; Artificial grass
- Baler twines, packaging twines and ropes
- Brush and broom filling and technical applications
Additives
Density: 0.9
Antioxidant package
| Typical Properties | Value | Unit | Method |
|---|---|---|---|
| Physical | |||
| Melt Flow Rate (230 °C, 2.16 kg) | 6.0 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D1505 |
| Mechanical | |||
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Tensile Strength at Yield | 32 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 8 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 °C | 40 | J/m | ASTM D256 |
| Thermal | |||
| Vicat softening point (10N) | 152 | °C | ASTM D1525 |
| H.D.T. (0.45 MPa) | 84 | °C | ASTM D648 |
| Accelerated oven ageing in air at 150 °C | 360 | hours | ASTM D3012 |